Electrode Aluminom na Aluminom Alloy
L109
GB/T E1100
AWS A5.3 E1100
Nkọwa: L109 bụ elektrọd aluminom dị ọcha nke nwere mkpuchi nnu. Jiri DCEP (elektrọd direct current positive). Gbalịa iji obere arc iji wedata ya.
Ngwa: A na-eji ya agbado efere aluminom na ihe mkpuchi aluminom dị ọcha.
Ngwakọta kemịkalụ nke ígwè weld(%):
| Si+Fe | Cu | Mn | Zn | Al | Ndị ọzọ |
| ≤0.95 | 0.05 ~ 0.20 | ≤0.05 | ≤0.10 | ≥99.0 | ≤0.15 |
Njirimara mekaniki nke igwe weld:
| Ihe nnwale | Ike ọdụdọ Mpa |
| Ekwere nkwa | ≥80 |
Ugbu a akwadoro:
| Dayameta mkpanaka （mm) | 3.2 | 4.0 | 5.0 |
| Ịgbado ọkụ ugbu a (A) | 80 ~ 100 | 110 ~ 150 | 150 ~ 200 |
Rịba ama:
1. Ọ dị mfe iji mmiri metụta elektrọd ahụ, yabụ e kwesịrị ịchekwa ya n'ime akpa akọrọ nke ikuku na-agaghị emebi emebi n'ihi mmiri; a ga-eme ka elektrọd ahụ sie ike na ihe dị ka 150°C maka awa 1 ruo 2 tupu ịgbado ọkụ;
2. A ga-eji efere nkwado tupu ịgbado ọkụ, a ga-emekwa ịgbado ọkụ mgbe e kpochara ọkụ ruo 200 ~ 300°C dịka ọkpụrụkpụ nke ịgbado ọkụ si dị; mkpanaka ịgbado ọkụ kwesịrị ịdị n'akụkụ elu nke ịgbado ọkụ ahụ, akịrịka kwesịrị ịdị mkpụmkpụ dịka o kwere mee, a ga-emekwa mgbanwe nke mkpanaka ịgbado ọkụ ngwa ngwa;
3. A ga-eji mmanụ na ihe ndị na-adịghị ọcha hichaa ihe e ji agwakọta ihe ahụ tupu a kụnye ya, a ga-ewepụkwa ihe e ji kpara ya nke ọma mgbe a kụnyechara ya, ma jiri uzuoku ma ọ bụ mmiri ọkụ sachaa ya.
E guzobere Wenzhou Tianyu Electronic Co., Ltd. n'afọ 2000. Anyị anọwo na-emepụta elektrọd ịgbado ọkụ, mkpanaka ịgbado ọkụ, na ihe oriri ịgbado ọkụ ruo ihe karịrị afọ 20.
Ngwaahịa anyị bụ isi gụnyere elektrọd ịgbado ígwè anaghị agba nchara, elektrọd ịgbado ígwè carbon, elektrọd ịgbado ígwè dị ala, elektrọd ịgbado ọkụ n'elu, elektrọd ịgbado ígwè nickel & cobalt, waya ịgbado ígwè dị nro na nke dị ala, waya ịgbado ígwè anaghị agba nchara, waya ndị nwere ihe mkpuchi gas, waya ịgbado ígwè aluminom, waya ịgbado arc mmiri, waya ịgbado ígwè nickel & cobalt, waya ịgbado ígwè brass, waya ịgbado ígwè TIG & MIG, elektrọd tungsten, elektrọd ịgbado ígwè, na ngwa ịgbado ígwè ndị ọzọ na ihe oriri.